Sinopec Factory Direct Sale Crystal Epoxy Resin Ab Glue for Flooring

• Customization: Available
• CAS No.: 1675-54-3
• Bonding Function: High Temperature Resistant Adhesive
• Model NO.: FL210
• Morphology: Transparent Liquid
• Application: Woodworking
• Material: Epoxy
• Classification: Room Curing
• Main Agent Composition: Epox Resin
• Characteristic: Solvent-Free
• Color: Clear
• Curing Condition: Room Temperature Curing
• Transport Package: 5kg/Drum
• Trademark: Sinopec
• Origin: Hunan
• HS Code: 3506912000
• Production Capacity: 3000000

Product Description

Product Description

 

FL210 epoxy system of Hunan petrochemical Co., Ltd consists of low-viscosity, high- strength epoxy resin and toughness curing agent, with high transparency, good toughness, bonding strength and other characteristics; can be widely used in art flooring, tile joints and other fields.

 

Basic parameters

 

Resin	FL-210A	Referenced standard
Appearance	Colorless transparent liquid	-
Epoxy equivalent[g/eq]	1500-2000	GB/T 22314-2008
Viscosity at 25ºC[mPa·s]	195-215	GB/T 4612-2008
Curing agent	FL-210B	Referenced standard
Appearance	Colorless transparent liquid	-
Viscosity at 25ºC[mPa·s]	800-1000	GB/T 22314-2008

 

Technological parameters

Mixing ratio (by weight)	FL-210A : FL-210B = 2:1
Mixing viscosity (25ºC)	1000-2000 mPa·s
Applicable period (25ºC,100g)	60-120 mins
Initial curing(25ºC)	Approx. 8-10 hours at room temperature
Final curing (25ºC)	Approx. 48-72 hours at room temperature
Operating temperature range	10ºC-70ºC
Points for attention	The amount of glue should be adjusted according to the operable time and the amount of glue used. Please keep the glue container clean and weigh it accurately according to the weight ratio of component A and B. Stir it fully clockwise along the inner wall of the container and remove the air bubbles after vacuuming. The lid of the barrel must be sealed after the use of B glue to avoid the product being scrapped due to moisture absorption.

 

Casting Properties

Hardness	shoreD	45-60
Bending strength	MPa	60-90
Glass transition temperature	ºC	50-70
Typical properties and shouldn't be regarded as a product specification.

 

Storage and shelf life

1. FL-210A epoxy resin has a chemical use deadlines of 12 months under storage conditions of 25ºC to 35ºC, dry and in the original sealed package.
2. FL-210B curing agent should be put in the original package, placed in a dry and cool place, avoid direct sunlight, the temperature is not higher than 30ºC, its chemical properties can be maintained for 6 months unchanged, high temperature and direct sunlight will accelerate the yellowing of the product.

 